Edge retention isn't exactly something that you should need to worry about with this material whatsoever but so far I would have to recommend 20° dps or more. This is where you have to ignore some of the CATRA results that you would use with steel alloys.Toker wrote: ↑Mon Mar 18, 2024 10:06 pmOptimum angle for durability and edge retention. I can't speak for everyone, but that's the only thing that interests me about this material.hollowt1pz wrote: ↑Mon Mar 18, 2024 5:42 pmPerformance graphics or just raw data and photos/video? I'd probably say the former is a bit superfluous. What would you guys prefer?
Edit: Correction - my recommendation after some more thought about it would swap to 17.5-22.5° ps. It's not going to work like steel.. impacts are going to soften the material, so it's going to 'chip' very different than steel.. you kinda want to expect it to chip after enough use regardless, so while to me, 22.5dps is .. quite fat? This stuff isn't going to perform much differently than it would at 17.5dps like steel, thus my current recommendation. (Everyone I know has their own opinions, someone smarter than me disagrees but it's under the same principle as far as I am educated)
Michael